Ionic liquids that sterilize and prevent biofilm formation in skin wound healing devices

ABSTRACT

Compositions for enhancing wound healing are disclosed herein. Also disclosed are methods of making the compositions and methods of using the compositions for the prevention of biofilm formation and for the inhibition of pathogen growth and proliferation.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of U.S. patent application Ser. No. 16/368,038, filed on Mar. 28, 2019, which is a continuation of U.S. patent application Ser. No. 15/725,213, filed Oct. 4, 2017, which issued as U.S. Pat. No. 10,293,080 on May 21, 2019, which claims the benefit of priority to U.S. Provisional Application No. 62/404,369, filed Oct. 5, 2016, the disclosure of each of which is hereby expressly incorporated by reference in its entirety.

FIELD

The present disclosure relates generally to the field of wound healing. In particular, the disclosure relates to compositions for enhancing wound healing. Such compositions include an ionic liquid and a protein scaffold. The compositions can be impregnated into a wound healing device, such as a bandage, or dressing. The disclosure also relates to methods of making the compositions and using the compositions to treat wounds.

BACKGROUND

Wound healing is a complex cascade of events that attempts to maintain homeostasis in the wounded tissue. Closing of the wound is essential to the healing process as it protects the tissue itself from infection with foreign agents, such as opportunistic bacterial pathogens. Biofilms established by these pathogens are a common cause of chronic infections that slow the process of wound healing. The bacterial biofilms themselves are challenging to eliminate with conventional antibiotics due to an extensive exopolymeric layer covering the pathogen that limits diffusion of these drugs into the biofilm. Ionic liquids, such including deep eutectic solvents (DESs), is a family of molecules with diverse chemical properties.

When considering dermal wound healing, there is a driving need for the organism to close the wound from the environment as a form of protection. If the wound does not close in a sufficient amount of time, foreign agents can enter the body and have serious pathological effects. Additionally, in a clinical environment, various devices and/or materials are implanted into the integument (skin) to treat the skin or other tissues and organs. In these cases, altering the skin environment can present significant risks to the organism (patient) for bacteria, viral, or fungal contamination of the compromised skin.

A specific patient population at significant risk for open wound contamination by biofilm formation includes unmanaged diabetic patients who develop chronic, non-healing wounds. Diabetic foot ulcers affect an estimated 1.4 million people in the U.S., resulting in enormous health care expenditures estimated at more than $176 billion per year for 2012 (Margolis et al., Incidence of diabetic foot ulcer and lower extremity amputation among Medicare beneficiaries, 2006 to 2008, Data Points Publication Series, Feb. 17, 2011; Mathieu, D. (Ed.). Handbook on hyperbaric medicine (Vol. 27). New York: Springer. 2006; Menke, et al., Impaired wound healing. Clinics in dermatology, 25(1), 19-25. 2007. Washington health system: Washington hospital. (2014)). Diabetic patients who have chronic disease may experience persistent wounds for months to years. Furthermore, if healing occurs, the healed tissue has substantial scarring and the scar may fail, resulting in recurrence of the ulcer.

Chronic diabetic wounds pose different pathophysiological abnormalities that contribute to a complex wound microenvironment that varies from the “normal” wound healing cascade (Falanga, V. Wound healing and its impairment in the diabetic foot. The Lancet, 366(9498), 1736-1743. 2005). This variation leads to a loss of synchrony of events indicative of rapid healing. There is a pathogenic triad of events that are predisposed in diabetic patients consisting of neuropathy, ischemia and trauma that hinders normal healing. Each of these factors affects each other in a way that results in an impaired ability to fight infection and presents difficulties in closing chronic skin wounds.

Currently, the clinical treatment of full thickness skin wounds presents a significant challenge. Therapies for the treatment of these skin wounds include autologous tissue grafts and fat transplantation (replacing burnt or severely traumatized tissue with a patient's own skin & fat tissue—taken from a distant site), and alloplastic (synthetic) implants. However, these methods present significant problems for the patient including donor site morbidity, implant migration, rupture, volume reduction, and foreign body reaction (Sterodimas, Aris, et al. Tissue engineering with adipose-derived stem cells (ADSCs): current and future applications. Journal of Plastic, Reconstructive & Aesthetic Surgery 63.11: 1886-1892, 2010; Stosich, et al. Adipose tissue engineering from human adult stem cells: clinical implications in plastic and reconstructive surgery. Plastic and reconstructive surgery 119.1: 71, 2007).

Furthermore, a lack of subcutaneous adipose tissue in full thickness skin wounds contributes to the aesthetically unappealing post-operative appearance (Shill K, et al. (2011) Ionic liquid pretreatment of cellulosic biomass: enzymatic hydrolysis and ionic liquid recycle. Biotechnology and bioengineering 108(3):511-520). There remains a major clinical demand for better methods of skin tissue healing of diabetic foot ulcers but also following severe burns, tumor excision, and trauma (Sterodimas, Aris, et al. Tissue engineering with adipose-derived stem cells (ADSCs): current and future applications. Journal of Plastic, Reconstructive & Aesthetic Surgery 63.11: 1886-1892, 2010).

In the clinical treatment of wounds, it is well established that open skin wounds colonize with bacteria; therefore, optimized wound care targets rapid wound closure in efforts to prevent infection and possible sepsis in severe cases (Wysocki, Annette B. Evaluating and managing open skin wounds: colonization versus infection. AACN Advanced Critical Care 13.3: 382-397, 2002). Today, wound care to prevent progression from colonization to infection remains the paramount objective of health care providers. However, this progression has become progressively difficult to combat due to emergent antimicrobial resistance (Davis, S. C., et al. Microscopic and physiologic evidence for biofilm-associated wound colonization in vivo. Wound Repair and Regeneration, 2008, 16: 23-29).

SUMMARY

The present disclosure generally relates to wound care compositions and methods of making and using the same.

Accordingly, some embodiments provided herein relate to a wound care composition. In some embodiments, the wound care composition includes an ionic liquid (IL) and a neutral species, and a protein scaffold that includes a protein solution. In some embodiments, the ionic liquid is present in an amount of about 0.01% w/w to about 99% w/w, such as 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or 99% w/w, or greater, or a value within a range defined by any two of the aforementioned values. In some embodiments, the IL is choline geranate (CAGE), choline citronellate, or choline urea. In some embodiments, the wound care composition is incorporated with or impregnated into or coated onto a wound dressing, a bandage, a gauze, a patch, a pad, tape, or a wrap. In some embodiments, the ionic liquid is present in an amount of about 40% w/w. In some embodiments, the protein solution comprises collagen, albumin, casein, fibrin, fibroin, gelatin, keratin, elastin, tropoelastin, or combinations thereof. In some embodiments, the protein scaffold is electrospun. In some embodiments, the protein solution is present in an amount of about 1% w/v to about 20% w/v. In some embodiments, the protein scaffold is present in an amount of about 10% w/v. In some embodiments, the wound care composition includes IL in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the wound care composition includes choline geranate in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the wound care composition includes choline citronellate in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the neutral species comprises farnesol, linalool, carvacrol, geranic acid, citronellic acid, cinnamaldehyde, eugenol, or combinations thereof. In some embodiments, the wound care composition further includes an antibiotic, a steroid, an analgesic, a cannabinoid, a growth factor, or a combination thereof.

Some embodiments provided herein relate to a wound dressing. In some embodiments, the wound dressing includes any one of the compositions as described herein and a wound dressing material. Thus, for example, the wound dressing may include a wound care composition that includes an ionic liquid (IL) and a neutral species, and a protein scaffold that includes a protein solution. In some embodiments, the ionic liquid is present in an amount of about 0.01% w/w to about 99% w/w, such as 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or 99% w/w, or greater, or a value within a range defined by any two of the aforementioned values. In some embodiments, the IL is choline geranate (CAGE) or choline citronellate. In some embodiments, the wound care composition is incorporated with or impregnated into or coated onto a wound dressing, a bandage, a gauze, a patch, a pad, tape, or a wrap. In some embodiments, the ionic liquid is present in an amount of about 40% w/w. In some embodiments, the protein solution comprises collagen, albumin, casein, fibrin, fibroin, gelatin, keratin, elastin, tropoelastin, or combinations thereof. In some embodiments, the protein scaffold is electrospun. In some embodiments, the protein solution is present in an amount of about 1% w/v to about 20% w/v. In some embodiments, the protein scaffold is present in an amount of about 10% w/v. In some embodiments, the wound care composition includes IL in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the wound care composition includes choline geranate in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the wound care composition includes choline citronellate in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin. In some embodiments, the neutral species comprises farnesol, linalool, carvacrol, geranic acid, citronellic acid, cinnamaldehyde, eugenol, or combinations thereof.

In some embodiments, the wound dressing material is a bandage, a wipe, a sponge, a mesh, a dressing, a gauze, a patch, a pad, tape, or a wrap. In some embodiments, the wound care composition is present in an amount of about 0.005% v/w to about 2% v/w, such as 0.005, 0.006, 0.007, 0.008, 0.009, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, or 2% volume of wound care composition/weight wound dressing material (vol/w), or greater, such as 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 30, 40, or 50% vol/w. In some embodiments, the wound care composition is present in an amount of about 0.625% v/w. In some embodiments, the wound care composition is incorporated into or coated onto or impregnated with the wound dressing material.

These features, together with other features herein further explained, are described in greater detail in the following description of the drawings and detailed description.

BRIEF DESCRIPTION OF THE DRAWINGS

The foregoing and other features of the present disclosure will become more fully apparent from the following description, taken in conjunction with the accompanying drawings. Understanding that these drawings depict only some embodiments in accordance with the disclosure and are therefore, not to be considered limiting of its scope, the disclosure will be described with additional specificity and detail through use of the accompanying drawings.

FIG. 1 illustrates the chemical components of one embodiment of ionic liquids (ILs).

FIG. 2 depicts a graphical representation of the ability of various ionic liquids to kill a biofilm of P. aeruginosa. BL=bleach and NT=no treatment. Percent biofilm survival after treatment is shown in the Inset on a log 10 scale to show differences between the most efficacious ILs. Choline geranate (CAGE) is shown as Ionic Liquid 11.

FIG. 3 depicts a scanning electron micrograph of an electrospun gelatin (5% w/v) scaffold, spun at a flow rate of 0.8 mL/hr, with an electric field of 2.91 kV/m.

FIG. 4 shows an image of a 0.2% w/v ionic liquid with gelatin scaffold during electrospinning.

FIG. 5 shows an image of a 1.0% w/v ionic liquid with gelatin scaffold during electrospinning.

FIG. 6A shows an image of an electrospun product having 10% w/v gelatin scaffold in hexafluoro-2-propanol (HFIP), spun at 30V, at a flow rate of 1 mL/hr, with a distance of the needle to target of 12 cm, at 26° C. in 18% humidity. FIG. 6B shows an image of an electrospun product having 10% w/v gelatin scaffold in HFIP plus 0.2% ionic liquid, spun at 25V, at a flow rate of 1 mL/hr, with a distance of the needle to target of 9 cm, at 26° C. in 18% humidity. FIG. 6C shows an image of an electrospun product having 10% w/v gelatin scaffold in HFIP plus 0.7% ionic liquid, spun at 25V, at a flow rate of 1 mL/hr, with a distance of the needle to target of 9 cm, at 26° C. in 18% humidity. FIG. 6D shows an image of an electrospun product having 10% w/v gelatin scaffold in HFIP plus 1.0% ionic liquid, spun at 25V, at a flow rate of 1 mL/hr, with a distance of the needle to target of 9 cm, at 26° C. in 18% humidity. Each of FIGS. 6A-6D show the scaffold before being removed from the foil (left) and after removal from foil (right).

FIG. 7 depicts structures of geranate (top left) and choline (top right), with an NMR spectrum of choline geranate (CAGE).

FIG. 8 depicts NMR spectra of the ionic liquid-incorporated scaffolds, indicating the presence of choline geranate incorporated scaffold (top), compared to choline geranate (CAGE) alone (bottom).

FIG. 9A depicts effects of a particular ionic liquid that includes choline geranate (CAGE) against P. aeruginosa on gauze. FIG. 9B depicts the percentage of P. aeruginosa colonies remaining on the gauze at 30 minutes or two hours following treatment (*=p<0.05, **=p<0.01, ***=p<0.001).

FIG. 10A depicts effects of CAGE against Enterococcus on gauze. FIG. 10B depicts the percentage of Enterococcus colonies remaining on the gauze at 30 minutes or two hours following treatment (*=p<0.05, **=p<0.01, ***=p<0.001).

FIG. 11A depicts effects of CAGE against K. pneumoniae on gauze. FIG. 11B depicts the percentage of K. pneumoniae colonies remaining on the gauze at 30 minutes or two hours following treatment (*=p<0.05, **=p<0.01, ***=p<0.001).

FIG. 12A depicts effects of CAGE against methicillin-sensitive Staphylococcus aureus (MSSA) on gauze. FIG. 12B depicts the percentage of MSSA colonies remaining on the gauze at 30 minutes or two hours following treatment (*=p<0.05, **=p<0.01, ***=p<0.001).

FIGS. 13A and 13B graphically depict the effects of CAGE scaffolds on P. aeruginosa at 30 minutes (FIG. 13A) and 2 hours (FIG. 13B) after treatment.

FIGS. 14A and 14B graphically depict the effects of CAGE scaffolds on Enterococcus at 30 minutes (FIG. 14A) and 2 hours (FIG. 14B) after treatment.

FIGS. 15A and 15B depict micrographs showing human dermal neonatal fibroblasts (P9) on control scaffolds (FIG. 15A) or CAGE-incorporated scaffolds (FIG. 15B).

DETAILED DESCRIPTION

In the following detailed description, reference is made to the accompanying drawings, which form a part hereof. In the drawings, similar symbols typically identify similar components, unless context dictates otherwise. The illustrative embodiments described in the detailed description, drawings, and claims are not meant to be limiting. Other embodiments may be utilized, and other changes may be made, without departing from the spirit or scope of the subject matter presented herein. It will be readily understood that the aspects of the present disclosure, as generally described herein, and illustrated in the drawings, can be arranged, substituted, combined, separated, and designed in a wide variety of different configurations, all of which are explicitly contemplated herein.

As summarized above, aspects of the wound care compositions and methods making and using the compositions are provided herein.

It is to be understood that this disclosure is not limited to particular embodiments described, as such may, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular embodiments only, and is not intended to be limiting.

As will be apparent to those of skill in the art upon reading this disclosure, each of the individual embodiments described and illustrated herein has discrete components and features which may be readily separated from or combined with the features of any of the other several embodiments without departing from the scope or spirit of the present disclosure. Any recited method can be carried out in the order of events recited or in any other order that is logically possible. U.S. application Ser. No. 16/307,347 entitled “Antibiofilm Formulations” relates to methods and compositions comprising antibiofilm materials, and is hereby incorporated by reference in its entirety, and for the disclosure referenced herein.

Unless defined otherwise, technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the present disclosure belongs. For purposes of the present disclosure, the following terms are defined below.

In some embodiments, provided herein is a method of treating a skin wound. A method of treating a skin wound includes contacting a wound with a wound care composition. In some embodiments, the wound care composition includes an ionic liquid-incorporated scaffold. As used herein, a wound refers to a burn, an abrasion, a laceration, a lesion, an ulcer, or a sore. Wounds include diabetic foot ulcers, severe burns, tumor excision, or trauma. A wound includes damage to the skin, and can include, for example damage caused by trauma, burn, surgery, or other type of damage. In some embodiments, the method of treating a skin wound enhances wound healing, prevents pathogen biofilm formation, inhibits pathogen growth and proliferation, inhibits sepsis, and prophylactically prevents the formation of biofilm or growth of pathogens. In some embodiments, the wound is skin damage, a burn, an abrasion, a laceration, an incision, a sore, a puncture wound, a penetration wound, a gunshot wound, or a crushing injury.

In some embodiments, the wound healing composition is applied to the wound at least once daily. In some embodiments, the wound healing formulation is applied to the wound three times a day. In some embodiments, applying the wound healing formulation provides a wound healing rate that is accelerated in comparison to a healing rate of a non-treated wound. In some embodiments, the formulation is applied in an amount effective to accelerate wound healing, promote wound closure, or cause wound regression. In some embodiments, the applying the formulation reduces, attenuates, or prevents bacterial growth or infection in the wound. In some embodiments, the composition does not prevent human or mammalian cells from proliferating.

In some embodiments is provided a wound care composition that includes an ionic liquid and a protein scaffold. In some embodiments, the composition may be used alone, for example, for direct application to a wound. Thus, for example, the composition may be formulated as an ointment, a cream, a spray, a spritz, a mist, a liquid, a gel, a lotion, or a solution. In some embodiments, the composition may be topically applied to a wound. In some embodiments, the composition may be administered subcutaneously.

In some embodiments, the composition may be configured for incorporation into a wound dressing material, including a bandage, a wipe, a sponge, a mesh, a dressing, a gauze, a patch, a pad, tape, or a wrap, or other wound dressing material. The composition may be used to saturate, impregnate, cover, coat, or otherwise be incorporated into a wound dressing material.

As referred to herein, the term “ionic liquid” (IL) refers a family of molecules commonly composed of an organic alkyl cation paired with either an organic or inorganic anion. These materials all have a melting point below 100° C. and are frequently described as “molten salts”. The chemical nature of the cation and anion components of an IL are readily modified, and as such, the physiochemical properties of the salt as a whole can be “tuned” for optimal use within a variety of applications (Hassan et al., Studies on the dissolution of glucose in ionic liquids and extraction using the antisolvent method. Environmental science & technology 47(6):2809-2816, 2013; Frederix M, et al., Development of a native Escherichia coli induction system for ionic liquid tolerance. PloS one 9(7):e101115, 2014; Eisenberg, Ionic interactions in biological and physical systems: a variational treatment. Faraday discussions 160:279-296, 2013; Cao Y, et al., Separation of soybean isoflavone aglycone homologues by ionic liquid-based extraction. Journal of agricultural and food chemistry 60(13):3432-3440, 2012; De Diego et al., A recyclable enzymatic biodiesel production process in ionic liquids. Bioresource technology 102(10):6336-6339, 2012); each of which is incorporated by reference herein in its entirety, and for the disclosure referenced herein). As used herein, “deep Eutectic Solvents” (DESs) are broadly defined as a mixture of charged and neutral species, either in equimolar or imbalanced ratios, that, when combined, have a much lower melting point than the individual component. DESs are mixtures of compounds and neutral molecules and ILs are themselves ionic compounds. The ionic liquid described herein, including DESs are intimately related on a chemical level and both are considered part of a larger class of molecules.

A number of ILs have shown a propensity to disrupt the noncovalent bonds within the structure of recalcitrant biopolymers such as cellulose or keratin (Lovejoy, et al. (2011) Tetraalkylphosphonium-Based Ionic Liquids for a Single-Step Dye Extraction/MALDI MS Analysis Platform. Anal Chem 83(8):2921-2930; Lovejoy et al. (2012) Single-Pot Extraction-Analysis of Dyed Wool Fibers with Ionic Liquids. Anal Chem 84(21):9169-9175; Shill K, et al. (2011) Ionic liquid pretreatment of cellulosic biomass: enzymatic hydrolysis and ionic liquid recycle. Biotechnology and bioengineering 108(3):511-520; each of which is incorporated by reference herein in its entirety, and for the disclosure referenced herein).

This aspect of IL chemistry has played an important role in the processing, disruption and dissolution of biopolymers for applications in renewable energy and forensics (Zhang J, et al. (2014) Understanding changes in cellulose crystalline structure of lignocellulosic biomass during ionic liquid pretreatment by XRD. Bioresource technology 151:402-405; Uju, et al. (2013) Peracetic acid-ionic liquid pretreatment to enhance enzymatic saccharification of lignocellulosic biomass. Bioresource technology 138:87-94; Varanasi P, et al. (2013) Survey of renewable chemicals produced from lignocellulosic biomass during ionic liquid pretreatment. Biotechnology for biofuels 6(1):14; Lovejoy, et al. (2011) Tetraalkylphosphonium-Based Ionic Liquids for a Single-Step Dye Extraction/MALDI MS Analysis Platform. Anal Chem 83(8):2921-2930; Lovejoy, et al. (2012) Single-Pot Extraction-Analysis of Dyed Wool Fibers with Ionic Liquids. Anal Chem 84(21):9169-9175; each of which is incorporated by reference herein in its entirety, and for the disclosure referenced herein).

The ability of ILs to disrupt biopolymers has also enabled their use as novel antibiotic agents that specifically target bacterial biofilms and have a bactericidal effect in general. Biofilms are communities of microbes that secrete a thick layer of exopolymeric material (including polysaccharides, proteins and nucleic acids) that effectively serve as a physical barrier to treatment with antibiotics (Donlan et al. (2001) Biofilms and device-associated infections. Emerg Infect Dis 7(2):277-281; Flemming et al. (2010) The biofilm matrix. Nature Reviews Microbiology 8(9):623-633; each of which is incorporated by reference herein in its entirety, and for the disclosure referenced herein). Typical applications of prescribed antibiotics do not efficiently pass through this physical barrier, and thus, biofilm bacteria are often 500-1000 times less susceptible to antibiotic treatment than their planktonic counterparts. Bacterial biofilms are responsible for most hospital-acquired infections, and the CDC has estimated the cost of combatting these maladies alone exceeds $10 billion per year (Bickers et al. (2006) The burden of skin diseases: 2004—A joint project of the American Academy of Dermatology Association and the Society for Investigative Dermatology. J Am Acad Dermatol 55(3):490-500). Antibacterial ILs disrupt the biofilm's protective exopolymeric layer and re-enable efficient antibiotic delivery to the cells within it, and sometimes have antibacterial properties themselves (Zakrewsky et al. (2014) Ionic liquids as a class of materials for transdermal delivery and pathogen neutralization. P Natl Acad Sci USA 111(37):13313-13318; Lovejoy et al. (2012) Utilization of Metal Halide Species Ambiguity to Develop Amorphous, Stabilized Pharmaceutical Agents As Ionic Liquids. Cryst Growth Des 12(11):5357-5364; each of which is incorporated by reference herein in its entirety, and for the disclosure referenced herein).

The development of ionic liquid-modified wound healing scaffolds will render the scaffolds themselves resistant to contamination with biofilms and enhance healing in difficult to treat patients. ILs are capable of preventing biofilm formation on a wound healing device without changing the structure and efficacy of the device.

Antibiofilm ionic liquids and deep eutectic solvents of particular interest are new deep eutectic systems, eutectic systems, or binary systems that incorporate isoprenoid acids such as citronellic acid, nerolic acid, other naturally occurring isoprenoid acids, or chemical derivatives of these groups, such as saturated or saturated and unbranched hydrocarbon derivatives. Numerous isoprenoid acids are already regarded as safe by the FEMA. In addition to geranate ions, other ions or ion sources suitable for use include but are not limited to citronellate, cinnamate, gibberelate, abietate, and others that act in a similar manner to geranate.

Accordingly, in some embodiments, a composition is provided having an ionic liquid (IL) and a neutral species, and a protein scaffold that includes a protein solution. In some embodiments, the IL is choline geranate (CAGE), choline citronellate, or choline urea. In some embodiments, the neutral species is any neutral species as disclosed herein. In some embodiments, the compositions further include an antibiotic, a steroid, an analgesic, a cannabinoid, and/or a growth factor. In some embodiments, the IL compositions may only include a neutral species.

An antibiotic may include, for example, any antibiotic suitable for wound care compositions having antimicrobial properties. Such antibiotics may include, for example, Amikacin disulfate salt, Amikacin hydrate, Anisomycin from Streptomyces griseolus, Apramycin sulfate salt, Azithromycin, Blasticidine S hydrochloride, Brefeldin A, Brefeldin A from Penicillium brefeldianum, Butirosin sulfate salt, Butirosin A from Bacillus vitellinus, Chloramphenicol, Chloramphenicol base, Chloramphenicol succinate sodium salt, Chlortetracycline hydrochloride, Chlortetracycline hydrochloride from Streptomyces aureofaciens, Clindamycin 2-phosphate, Clindamycin hydrochloride, Clotrimazole, Cycloheximide from microbial, Demeclocycline hydrochloride, Dibekacin sulfate salt, Dihydrostreptomycin sesquisulfate, Dihydrostreptomycin solution, Doxycycline hyclate, Duramycin from Streptoverticillium cinnamoneus, Emetine dihydrochloride hydrate), Erythromycin, Erythromycin USP, Erythromycin powder, Erythromycin, Temephos, Erythromycin estolate, Erythromycin ethyl succinate, Erythromycin standard solution, Erythromycin stearate, Fusidic acid sodium salt, G 418 disulfate salt, G 418 disulfate salt powder, G 418 disulfate salt solution liquid, Gentamicin solution liquid, Gentamicin solution, Gentamicin sulfate Micromonospora purpurea, Gentamicin sulfate salt, Gentamicin sulfate salt powder USP, Gentamicin-Glutamine solution liquid, Helvolic acid from Cephalosporium caerulens, Hygromycin B Streptomyces hygroscopicus, Hygromycin B Streptomyces hygroscopicus powder, Hygromycin B solution Streptomyces hygroscopicus, Josamycin, Josamycin solution, Kanamycin B sulfate salt, Kanamycin disulfate salt from Streptomyces kanamyceticus, Kanamycin monosulfate from Streptomyces kanamyceticus, Kanamycin monosulfate from Streptomyces kanamyceticus powder USP, Kanamycin solution from Streptomyces kanamyceticus, Kirromycin from Streptomyces collinus, Lincomycin hydrochloride, Lincomycin standard solution, Meclocycline sulfosalicylate salt, Mepartricin, Midecamycin from Streptomyces mycarofaciens, Minocycline hydrochloride crystalline, Neomycin solution, Neomycin trisulfate salt hydrate, Neomycin trisulfate salt hydrate powder, Neomycin trisulfate salt hydrate USP powder, Netilmicin sulfate salt, Nitrofurantoin crystalline, Nourseothricin sulfate, Oleandomycin phosphate salt, Oleandomycin triacetate, Oxytetracycline dihydrate, Oxytetracycline hemicalcium salt, Oxytetracycline hydrochloride, Paromomycin sulfate salt, Puromycin dihydrochloride from Streptomyces alboniger, Rapamycin from Streptomyces hygroscopicus, Ribostamycin sulfate salt, Rifampicin, Rifamycin SV sodium salt, Rosamicin Micromonospora rosaria, Sisomicin sulfate salt, Spectinomycin dihydrochloride hydrate, Spectinomycin dihydrochloride hydrate powder, Spectinomycin dihydrochloride pentahydrate, Spiramycin, Spiramycin from Streptomyces sp., Spiramycin solution, Streptomycin solution, Streptomycin sulfate salt, Streptomycin sulfate salt powder, Tetracycline, Tetracycline hydrochloride, Tetracycline hydrochloride USP, Tetracycline hydrochloride powder, Thiamphenicol, Thiostrepton from Streptomyces azureus, Tobramycin, Tobramycin sulfate salt, Tunicamycin A1 homolog, Tunicamycin C2 homolog, Tunicamycin Streptomyces sp., Tylosin solution, Tylosin tartrate, Viomycin sulfate salt, Virginiamycin M1, (S)-(+)-Camptothecin, 10-Deacetylbaccatin III from Taxus baccata, 5-Azacytidine, 7-Aminoactinomycin D, 8-Quinolinol crystalline, 8-Quinolinol hemisulfate salt crystalline, 9-Dihydro-13-acetylbaccatin III from Taxus canadensis, Aclarubicin, Aclarubicin hydrochloride, Actinomycin D from Streptomyces sp., Actinomycin I from Streptomyces antibioticus, Actinomycin V from Streptomyces antibioticus, Aphidicolin Nigrospora sphaerica, Bafilomycin A1 from Streptomyces griseus, Bleomycin sulfate from Streptomyces verticillus, Capreomycin sulfate from Streptomyces capreolus, Chromomycin A3 Streptomyces griseus, Cinoxacin, Ciprofloxacin BioChemika, cis-Diammineplatinum(II) dichloride, Coumermycin A1, Cytochalasin B Helminthosporium dematioideum, Cytochalasin D Zygosporium mansonii, Dacarbazine, Daunorubicin hydrochloride, Daunorubicin hydrochloride USP, Distamycin A hydrochloride from Streptomyces distallicus, Doxorubicin hydrochloride, Echinomycin, Echinomycin BioChemika, Enrofloxacin BioChemika, Etoposide, Etoposide solid, Flumequine, Formycin, Fumagillin from Aspergillus fumigatus, Ganciclovir, Gliotoxin from Gliocladium fimbriatum, Lomefloxacin hydrochloride, Metronidazole purum, Mithramycin A from Streptomyces plicatus, Mitomycin C Streptomyces caespitosus, Nalidixic acid, Nalidixic acid sodium salt, Nalidixic acid sodium salt powder, Netropsin dihydrochloride hydrate, Nitrofurantoin, Nogalamycin from Streptomyces nogalater, Nonactin from Streptomyces tsusimaensis, Novobiocin sodium salt, Ofloxacin, Oxolinic acid, Paclitaxel from Taxus yannanensis, Paclitaxel from Taxus brevifolia, Phenazine methosulfate, Phleomycin Streptomyces verticillus, Pipemidic acid, Rebeccamycin from Saccharothrix aerocolonigenes, Sinefungin, Streptonigrin from Streptomyces flocculus, Streptozocin, Succinylsulfathiazole, Sulfadiazine, Sulfadimethoxine, Sulfaguanidine purum, Sulfamethazine, Sulfamonomethoxine, Sulfanilamide, Sulfaquinoxaline sodium salt, Sulfasalazine, Sulfathiazole sodium salt, Trimethoprim, Trimethoprim lactate salt, Tubercidin from Streptomyces tubercidicus, 5-Azacytidine, Cordycepin, Formycin A, (+)-6-Aminopenicillanic acid, 7-Aminodesacetoxycephalosporanic acid, Amoxicillin, Ampicillin, Ampicillin sodium salt, Ampicillin trihydrate, Ampicillin trihydrate USP, Azlocillin sodium salt, Bacitracin Bacillus licheniformis, Bacitracin zinc salt Bacillus licheniformis, Carbenicillin disodium salt, Cefaclor, Cefamandole lithium salt, Cefamandole nafate, Cefamandole sodium salt, Cefazolin sodium salt, Cefinetazole sodium salt, Cefoperazone sodium salt, Cefotaxime sodium salt, Cefsulodin sodium salt, Cefsulodin sodium salt hydrate, Ceftriaxone sodium salt, Cephalexin hydrate, Cephalosporin C zinc salt, Cephalothin sodium salt, Cephapirin sodium salt, Cephradine, Cloxacillin sodium salt, Cloxacillin sodium salt monohydrate, D-Penicillamine hydrochloride, D-Cycloserine microbial, D-Cycloserine powder, Dicloxacillin sodium salt monohydrate, D-Penicillamine, Econazole nitrate salt, Ethambutol dihydrochloride, Lysostaphin from Staphylococcus staphylolyticus, Moxalactam sodium salt, Nafcillin sodium salt monohydrate, Nikkomycin, Nikkomycin Z Streptomyces tendae, Nitrofurantoin crystalline, Oxacillin sodium salt, Penicillic acid powder, Penicillin G potassium salt, Penicillin G potassium salt powder, Penicillin G potassium salt, Penicillin G sodium salt hydrate powder, Penicillin G sodium salt powder, Penicillin G sodium salt, Phenethicillin potassium salt, Phenoxymethylpenicillinic acid potassium salt, Phosphomycin disodium salt, Pipemidic acid, Piperacillin sodium salt, Ristomycin monosulfate, Vancomycin hydrochloride from Streptomyces orientalis, 2-Mercaptopyridine N-oxide sodium salt, 4-Bromocalcimycin A23187 BioChemika, Alamethicin Trichoderma viride, Amphotericin B Streptomyces sp., Amphotericin B preparation, Calcimycin A23187, Calcimycin A23187 hemi(calcium-magnesium) salt, Calcimycin A23187 hemicalcium salt, Calcimycin A23187 hemimagnesium salt, Chlorhexidine diacetate salt monohydrate, Chlorhexidine diacetate salt hydrate, Chlorhexidine digluconate, Clotrimazole, Colistin sodium methanesulfonate, Colistin sodium methanesulfonate from Bacillus colistinus, Colistin sulfate salt, Econazole nitrate salt, Hydrocortisone 21-acetate, Filipin complex Streptomyces filipinensis, Gliotoxin from Gliocladium fimbriatum, Gramicidin A from Bacillus brevis, Gramicidin C from Bacillus brevis, Gramicidin from Bacillus aneurinolyticus (Bacillus brevis), lonomycin calcium salt Streptomyces conglobatus, Lasalocid A sodium salt, Lonomycin A sodium salt from Streptomyces ribosidificus, Monensin sodium salt, N-(6-Aminohexyl)-5-chloro-1-naphthalenesulfonamide hydrochloride, Narasin from Streptomyces auriofaciens, Nigericin sodium salt from Streptomyces hygroscopicus, Nisin from Streptococcus lactis, Nonactin from Streptomyces sp., Nystatin, Nystatin powder, Phenazine methosulfate, Pimaricin, Pimaricin from Streptomyces chattanoogensis, Polymyxin B solution, Polymyxin B sulfate salt, DL-Penicillamine acetone adduct hydrochloride monohydrate, Polymyxin B sulfate salt powder USP, Praziquantel, Salinomycin from Streptomyces albus, Salinomycin from Streptomyces albus, Surfactin from Bacillus subtilis, Valinomycin, (+)-Usnic acid from Usnea dasypoga, (+−)-Miconazole nitrate salt, (S)-(+)-Camptothecin, 1-Deoxymannojirimycin hydrochloride, 1-Deoxynojirimycin hydrochloride, 2-Heptyl-4-hydroxyquinoline N-oxide, Cordycepin, 1,10-Phenanthroline hydrochloride monohydrate puriss., 6-Diazo-5-oxo-L-norleucine, 8-Quinolinol crystalline, 8-Quinolinol hemisulfate salt, Antimycin A from Streptomyces sp., Antimycin A1, Antimycin A2, Antimycin A3, Antipain, Ascomycin, Azaserine, Bafilomycin A1 from Streptomyces griseus, Bafilomycin B1 from Streptomyces species, Cerulenin BioChemika, Chloroquine diphosphate salt, Cinoxacin, Ciprofloxacin, Mevastatin BioChemika, Concanamycin A, Concanamycin A Streptomyces sp, Concanamycin C from Streptomyces species, Coumermycin A1, Cyclosporin A from Tolypocladium inflatum, Cyclosporin A, Econazole nitrate salt, Enrofloxacin, Etoposide, Flumequine, Formycin A, Furazolidone, Fusaric acid from Gibberella fujikuroi, Geldanamycin from Streptomyces hygroscopicus, Gliotoxin from Gliocladium fimbriatum, Gramicidin A from Bacillus brevis, Gramicidin C from Bacillus brevis, Gramicidin from Bacillus aneurinolyticus (Bacillus brevis), Gramicidin from Bacillus brevis, Herbimycin A from Streptomyces hygroscopicus, Indomethacin, Irgasan, Lomefloxacin hydrochloride, Mycophenolic acid powder, Myxothiazol BioChemika, N-(6-Aminohexyl)-5-chloro-1-naphthalenesulfonamide hydrochloride, Nalidixic acid, Netropsin dihydrochloride hydrate, Niclosamide, Nikkomycin BioChemika, Nikkomycin Z Streptomyces tendae, N-Methyl-1-deoxynojirimycin, Nogalamycin from Streptomyces nogalater, Nonactin .quadrature.80% from Streptomyces tsusimaensis, Nonactin from Streptomyces sp., Novobiocin sodium salt, Ofloxacin, Oleandomycin triacetate, Oligomycin Streptomyces diastatochromogenes, Oligomycin A, Oligomycin B, Oligomycin C, Oligomycin Streptomyces diastatochromogenes, Oxolinic acid, Piericidin A from Streptomyces mobaraensis, Pipemidic acid, Radicicol from Diheterospora chlamydosporia solid, Rapamycin from Streptomyces hygroscopicus, Rebeccamycin from Saccharothrix aerocolonigenes, Sinefungin, Staurosporine Streptomyces sp., Stigmatellin, Succinylsulfathiazole, Sulfadiazine, Sulfadimethoxine, Sulfaguanidine purum, Sulfamethazine, Sulfamonomethoxine, Sulfanilamide, Sulfaquinoxaline sodium salt, Sulfasalazine, Sulfathiazole sodium salt, Triacsin C from Streptomyces sp., Trimethoprim, Trimethoprim lactate salt, Vineomycin A1 from Streptomyces albogriseolus subsp., Tectorigenin, and Paracelsin Trichoderma reesei.

A steroid may include any steroid compound suitable in a wound care composition, including, for example, corticosteroids, progestrogens, androgens, estrogens, neurosteroids, aminosteroids, or secosteroids.

An analgesic may include any analgesic compound suitable in a wound care compositions, including, for example, a paracetamol, an NSAID, an opioid, or an analgesic adjuvant, or any other suitable analgesic, including combinations of analgesics.

A cannabinoid may include any compound within the class that acts upon cannabinoid receptors (such as on the endocannabinoid system) in cells. A cannabinoid can include a synthetic cannabinoid, a phytocannabinoid, or an endocannabinoid. In some embodiments, a cannabinoid includes cannabidiols (including cannabidiol, cannabidiolic acid, cannabidiol monomethylether, cannabidiorcol, cannabidivarin, or cannabidivarinic acid), tetrahydrocannabinols (including delta-9-tetrahydrocannabinol, delta-9-cis-tetrahydrocannabinol, delta-9-tetrahydrocannabinol-C4, delta-9-tetrahydrocannabinolic acid A, delta-9-tetrahydrocannabinolic acid B, delta-9-tetrahydrocannabinolic acid C4, delta-9-tetrahydrocannabiorcol, delta-9-tetrahydrocannabiocolic acid, delta-9-tetrahydrocannabivarin, delta-9-tetrahydrocannabivarinic acid, tryhydroxy-delta-9-tetrahydrocannabinol, delta-8-tetrahydrocannabinol, or delta-8-tetrahydrocannabinolic acid), cannabichromenes (including cannabichromene, cannabichromenenic acid, cannabichromevarin, cannabichromenvarinic acid), cannabigerols (including cannabigerol, cannabigerol monomethylether, cannabigerolic acid, cannabigerolic acid monomethylether, cannabinerolic acid, cannabigerovarin, or cannabigerovarinic acid), cannabielsoins (including cannabielsoin, cannabielsoic acid A, or cannabielsoic acid B), cannabinols or cannabinodiols (includiong cannabinodiol, cannabinodivarin, cannabinol, cannabinol methylether, cannabinol-C2, cannabinol-C4, cannabinolic acid, cannabiorcool, or cannabivarin), cannabitriols (including cannabitriol, cannabitriolvarin, 10-ethoxy-9-hydroxy-delta-6a-tetrahydrocannabinol, or 8,9-dihydroxy-delta-6a-tetrayhydrocannabinol), cannabicyclols, 10-oxo-delta-6a-tetrahydrocannabinol, cannabichromanon, cannabifuran, cannabiglendol, cannabiripsol, cannbicitran, dehydrocannabifuran, cannabicitran, or 3,4,5,6-tetrahydro-7-hydroxy-alpha-alpha-trimethyl-9-n-propyl-2,6-methano-2H-1-benzoxicin-5-methanol, or any analogue or derivative thereof.

A growth factor may include any growth factor, including, for example, epidermal growth factor (EGF), platelet derived growth factor (PDGF), fibroblast growth factor (FGF), transforming growth factors (TGF-α and TGF-β), nerve growth factor (NGF), erythropoietin (EPO), insulin-like growth factors (IGF-I and IGF-II), interleukin cytokines (IL-1α, IL-1β, IL-2, IL-3, IL-4, IL-5, IL-6, IL-7, IL-8, IL-9, IL-10, IL-11, IL-12, IL-13), interferons (IFN-α, IFN-β, and IFN-γ), tumor necrosis factors (TNFα and TNF-β), colony stimulating factors (GM-CSF and M-CSF).

While 1:1 equimolar pairings can advantageously be employed in an antibiofilm, 2:1 deep eutectic system formulations can also be employed. Data further indicates that the nature of the neutral species may be changed as well and may similarly potentiate the antibiofilm/antibacterial properties relative to the 1:1 mixture, or minimally does not elicit a marked loss of antibiofilm/antibacterial properties. For example, formulations that include the following neutral species are envisioned: protonated acids (e.g., isoprenoid acids), isoprenoid alcohols, and isoprenoid hydrocarbons. In addition to isoprenoids, other bioactive components can be included as well, e.g., phenylpropanoids (shikimate metabolites) or fatty acids. Formulations with protonated acids include 1:1 CAGE with citronellic acid or 1:1 choline citronellate (CACI) with geranic acid or citronellic acid. A CAGE or CACI scaffold can be provided with other acids, such as cinnamic acid, vanillic acid, gibberelic acid, derivatives of benzoic acid, or derivatives of salicylic acid. Other isoprenoid acids include absciscic acid, artesunate, carnosic acid, chenodeoxycholic acid, cholic acid, +/−chrysanthemic acid, deoxycholic acid, fusidic acid, glycocholic acid, isosteviol, isopimaric acid, isovaleric acid, phytanic acid, pristanic acid, steviol, a cannabinoid compound (e.g., tetrahydrocannabinic acid, cannabigerolic acid, Δ9-tetrahydrocanabinolic acid, cannabidiol, cannabidiolic acid, cannabichromenenic acid, cannabigerovarinic acid, tetrahydrocannabivaric acid, cannabidivarinic acid, cannabichromevarinic acid, nabilone, ajulemic acid), and ursolic acid.

Additionally, it is envisioned that other compounds may be used which include amcinonide, artemesin, artemether, artemotil, butamethasone, camphor, chrysanthone, citral, citronaldehyde, clobetasol propionate, clobetasone, cortisone, cortisol, cuminaldehyde, desonide, drospiranone, ethinyl estradiol, farnesyl acetate, fenchone, flucloronide, fludocortisone, fludroxycortide, fluocinolone acetonide, fluticasone, formocortal, halcinonide, halometasone, hydrocortisone, geranal acetate, geranial, geranylgeranyl acetone (teprenone), indometacin farnesil, α,β,γ-ionone, lavandulal acetate, linalool acetate, loteprednol, menthofuran, methone, methyl acetate, mometasone furoate, neral, nootkatone, R/S-perillyl aldehyde, perilla ketone, piperitone, prenamustine, prednisone, premarin, pulegone, +/−rose oxide, safranal, salvinorins A-J, trans-sorbrerol, synthetic progestogens, progestin, α/β-thujone, tocopherol acetate, triamcinolone acetonide, +/−verbenone, vetiver acetate, whiskey lactone, wine lactone, and zingerone.

Isoprenoid alcohols, often found in natural sources such as essential oils, may also be employed in formulations of the embodiments. Geraniol, citronellol, nerol and acylated myrcene (all extremely chemically similar) all have a very low toxicity/mutagenicity potential. Farnesol and linalool are known to be microbial signaling molecules, and geraniol is similarly bioactive. Furthermore, linear alcohols such as dolichol, geranylgeraniol, isophytol, cis/trans-nerolidol, retinol, and β-rhodinol may be suitable.

Common terpenoid alcohols with varied structures which are included as components in commercial products may be electrospun into a scaffold for uses as described herein. Camphor (oxidized isoborneol) and eucalyptol are common cough suppressants (e.g., Vicks Vap-o-rub and similar products). Humulone and isohumulone are bittering agents in beer, and also exhibit antibiofilm abilities. Carvone is an oxidized terpenoid alcohol found in black pepper. Additional examples of suitable cyclic alcohols include andrographolide, aphidicolin, α/β-bisabolol, α/β-cadinol, cafestol, capsidiol, carotol, +/−cis/trans-carveol, carnosol, carvacrol, carvone, cedrol, cholicalciferol, docetaxel, ergocalciferol, estradiol and associated derivatives, eucalyptol, feruginol, +/−fenchyl alcohol, ginkolides, guaiol, hinokitiol, humulone, ingenol mebutate, D/L-menthol, isoprenol, (−)-isoborneol, isohumulone, patchoulol, R/S perillyl alcohol, prenol, α/β-santalol, scleriol, testosterone and associated derivatives, tetrahydrocannabinol, α,β,γ-terpineol, α,β-terpeniol, terpine-4-ol, thioterpineol, thymol, α,β,δ,γ-tocopherol, verbenol, zeaxanthin, cannabigerol, Δ9-tetrahydrocannabinol, cannabidiol, cannabichromene, cannabigerivarin, tetrahydrocannabivarin, cannabidivarin, and cannabichromevarin.

Useful examples of isoprenoid hydrocarbons are provided below. Many of these are common additives in surface cleaners/disinfectants/sterilizers. Inclusion of these compounds in formulations of the embodiments can yield similar cleaning agents that can similarly break down into environmentally innocuous materials, e.g., for use as green cleaners for household use. Other hydrocarbons include bornane, cadalene, camphene, carinene, α-carotene, δ-carotene, cedrene, p-cymene, α,β,γ-guaiene, guaiazulene, humulene, isoprene, norbornane, ocimene, phellandrene, phytane, phytoene, sabinene, aqualene, squalene, terpinolene, terpinene, α,β-thujene, valencene, Vitamin K1, Vitamin K2 (MK-4), and Vitamin K2 (MK-7). Additional examples include D-limonene, α-pinene, α-farnesene, myrcene, bergamotene, and α-humulene.

Representative examples of phenylpropanoids include the following: cinnamaldehyde, cinnamyl alcohol, cinnamic acid, vanillin, vanillyl alcohol, and vanillic acid. Many bioactive molecules are derived from shikimate pathway metabolites as opposed to isoprenoids, and often possess antibacterial/antibiofilm abilities. The aldehydes below are found in essential oils and used commonly as flavorings, and alcohol and acid derivatives readily exist. Other examples of phenylpropanoids include eugenol, capsaicin, curcumin, salicylic acid, and protocatechuic acid.

Other compounds exhibiting stabilizing and preservative activity can be included in the disclosed formulations of the embodiments. These molecules include natural antioxidants and/or common preservatives such as vitamin E, tocopherol acetate, and the carotenoids, which are common vitamin nutraceuticals. Vitamin E and tocopherol acetate are also part of many cosmetics/skin lotions. Representative examples include α-tocopherol, α-tocopherol acetate, β-carotene, lutein, salicylic acid, and protocatechuic acid. Such stabilizers and preservatives can be included in a deep eutectic system, a eutectic system, or a binary system. When included, they can be used in any suitable concentration, e.g., 0.1% or less to 5% or more by volume, e.g., 1% to 2% by volume. In certain embodiments, such compounds can be present in equal portions to a 1:1 IL in order to make a 2:1 DES.

In some embodiments, compositions including an IL is added, incorporated, coated on, applied to, saturated with, impregnated with, covered with, or otherwise be incorporated or contacted with a wound dressing material in an amount of 0.005% to 2% volume IL to weight gauze (vol/w %), such as 0.005, 0.006, 0.007, 0.008, 0.009, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, or 2% volume of wound care composition/weight wound dressing material (vol/w %), or greater, such as 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 30, 40, or 50% vol/w or an amount within a range defined by any two of the aforementioned values. In some embodiments, the wound care composition is present in an amount of about 0.625% vol/w %. In some embodiments, the IL is contacted with a wound dressing in an amount of 0.05 μg per mg wound dressing material to 20 μg per mg wound dressing material, such as 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, or 20 μg/mg, or an amount within a range defined by any two of the aforementioned values. In some embodiments, the wound care composition is present in an amount of about 6.25 μg/mg. Thus, in some embodiments, the composition including an IL is incorporated into a wound dressing material, for example, to saturate, impregnate, cover, coat, or otherwise be incorporated into the wound dressing material. Coating can include, for example, dip coating or surface modifying a material with an IL.

In some embodiments, the amount of IL incorporated into an electrospun scaffold can be 0.01% w/w to about 99% w/w, such as 0.01, 0.05, 0.1, 0.5, 1.0, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, 90, 95, or 99% w/w or greater, or a value within a range defined by any two of the aforementioned values. In some embodiments, the IL is present in an amount of about 40% w/v.

Ionic liquids may also be used as carriers to incorporate other compounds such as drugs (e.g., antibiotics, hemorrheologic agents, antiplatelet agents, anti-inflammatory agents), compounds/proteins of interest (e.g., steroids, sterols, hormones, coloring agents, dyes, preservatives, antioxidants, flavorings, perfumes, analgesics (e.g., non-steroidal anti-inflammatory drugs, acetaminophen, cannabinoid compounds, opioid drugs, antihistamine drugs, among others known in the art to manage pain or discomfort), growth factors (e.g., platelet-derived growth factor-beta (PDGF-beta), transforming growth factor-beta (TGF-beta), platelet-rich plasma, basic fibroblast growth factor (bFGF), epidermal growth factor (EGF)), extracellular matrix proteins, collagen), or other medications. In such cases, the IL is mixed in an appropriate ratio with the other compound of interest and said IL mixture is then processed by electrospinning into a protein scaffold.

Ionic liquids may also be used as solvents to incorporate compounds that are otherwise insoluble in aqueous or electrospinning solvents into an electrospun scaffold by forming to form emulsions (or microemulsions, nanoemulsions) for incorporation into an electrospun scaffold. As known in the art, an emulsion comprises a mixture two or more liquids wherein said liquids are typically immiscible; this mixture is composed of finely dispersed droplets, such as micelles, of one liquid within the second liquid. In some embodiments, an insoluble compound is mixed with an IL to create an IL-based emulsion that is used as a carrier for the insoluble compound; this IL-emulsion may then be electrospun into a protein scaffold as described herein. In an additional embodiment, an IL-based emulsion is integrated into an electrospun protein scaffold to serve as a reservoir for controlled time release of a drug or other suitable compound.

As mentioned above, ILs may be used as solvents for insoluble compounds for the purposes of electrospinning the insoluble compound into a protein scaffold. In certain cases, it may be advantageous to remove the IL from the protein scaffold, leaving only the insoluble compound behind in the scaffold; based on the physicochemical properties of the IL, a corresponding solution may be used to wash out the IL from the scaffold without also removing the insoluble compound delivered into the scaffold by the IL.

As used herein, pathogens can include opportunistic pathogens associated with skin infections, including, for example, bacterial infections (including, for example, Staphylococcus aureus, Pseudomonas aeruginosa, methicillin resistant S. aureus (MRSA), Streptococcus pyogenes), viral infections, fungal infections, or yeast infections. In some embodiments, the compositions provided herein prevent pathogenic growth. In some embodiments, the compositions do not prevent human or mammalian cell proliferation. In some embodiments, the compositions do not prevent human or mammalian cells from adhering, associating with, or proliferating on a scaffold or surface.

As used herein a scaffold refers to a material that acts as a foundation or structure for the formulation of the wound care compositions as described herein. The scaffold may be a protein scaffold or a polysaccharide scaffold and may include a molecule for structural formation, including, for example any protein solution, including, for example, one or more of collagen, agarose, albumin, alginate, casein, elastin, fibrin, fibroin, fibronectin, gelatin, keratin, laminin, pectin, elastin, tropoelastin, cellulose, chitosan, chitin. In some embodiments, the wound care composition is prepared by electrospinning a protein scaffold incorporated with IL. In some embodiments, the amount of protein scaffold, can be 0.01%, 0.02%, 0.03%, 0.04%, 0.05%, 0.06%, 0.07%, 0.08%, 0.09%, 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1%, 2%, 3%, 4%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14%, 15%, 16%, 17%, 18%, 19% or 20% w/v or greater, or a value within a range defined by any two of the aforementioned values.

The protein scaffold can be in solution, for example, in a solvent. In some embodiments, the solvent is the IL. In some embodiments, the solvent is an organic solvent. In some embodiments, the organic solvent is a polyamide, a polyacrylonitrile, a polyacetal, a polyester, or a polyketone, or a combination thereof. In some embodiments, the organic solvent is ethanol, ethyl formate, hexafluoro-2-propanol (HFIP), cyclic ethers (tetrahydrofuran (THF), and 2,5-dimethylfuran (DMF)), acetone, acetates of C2 to C5 alcohol (such as ethyl acetate and butyl acetate), glyme or dimethoxyethane (monoglyme, ethyl glyme, diglyme, ethyl diglyme, triglyme, butyl diglyme, tetraglyme, dimethyl glycol, ethylene glycol dimethyl ether, dimethyl cellosolve, and DME), methylethyl ketone (butanone), dipropyleneglycol methyl ether, lactones (such as δ-valerolactone, γ-valerolactone, b-butyrolactone, g-butyrolactone), 1,4-dioxane, 1,3-dioxolane, ethylene carbonate, dimethylcarbonate, diethylcarbonate, benzene, toluene, benzyl alcohol, p-xylene, N-methyl-2-pyrrolidone, dimethylformamide, chloroform (trichloromethane, methyl trichloride), 1,2-dichloromethane (DCM), morpholine, dimethylsulfoxide (DMSO), hexafluoroacetone sesquihydrate (HFAS), anisole (methoxybenzene) and mixtures thereof.

Electrospun materials have been described since 1934 (Garg et al. Electrospinning jets and nanofibrous structures.” Biomicrofluidics 5.1: 013403, 2011). Since then a plethora of proteins and polymers have been electrospun into scaffolds for use in clinical and research realms. The principle behind electrospinning is to eject a solubilized protein through a charged nozzle onto an oppositely charged target. When the surface tension forces are balanced with the electric field, the protein droplet elongates forming a funnel shape known as a Taylor cone (Taylor. Electrically driven jets. Proceedings of the Royal Society of London A: Mathematical, Physical and Engineering Sciences. Vol. 313. No. 1515. The Royal Society, 1969). However, the stability of the cone was a problem until 1987 when Hayati discovered that semiconducting insulating liquids created more stability at higher voltages (Hayati et al., Investigations into the mechanisms of electrohydrodynamic spraying of liquids: I. Effect of electric field and the environment on pendant drops and factors affecting the formation of stable jets and atomization. Journal of Colloid and Interface Science 117.1: 205-221, 1987). The stable cone and ejection of the solubilized protein causes the solvent to evaporate before the target is reached and the creation of nanofibers being laid upon the target in a nonwoven pattern.

In 1971, Baumgarten determined that by varying the concentration of protein and changing the applied voltage, the diameter of the nanofibers could be manipulated, with a higher concentration producing larger continuous fibers and lesser concentrations producing shorter and finer fibers (Baumgarten, Electrostatic spinning of acrylic microfibers. Journal of colloid and interface science 36.1: 71-79, 1971).

Provided herein are electrospinning methods for the creation of novel protein scaffolds that serve as wound healing agents. These scaffolds are fabricated using native skin proteins and as a result, they more closely match the composition and architecture of skin, thereby enhancing wound healing.

The novelty of the embodiments and alternatives described herein includes the combination of ILs and protein scaffolds to enhance the wound healing process. The development of IL-modified wound healing scaffolds mitigates biofilm formation on these scaffolds and enhances healing in difficult to treat patients.

As used herein, the term “treatment” refers to an intervention made in response to a wound, such as a burn or other wound, including difficult to treat wounds, in a subject in need. The aim of treatment may include, but is not limited to, one or more of the alleviation or prevention of symptoms, slowing or stopping the progression or worsening of a wound, enhancement of the wound healing, and the remission of the wound. In some embodiments, “treatment” refers to both therapeutic treatment and prophylactic or preventative measures. Those in need of treatment include those already affected by a wound as well as those in which an infection of the wound is to be prevented.

As used herein, the terms “treating,” “treatment,” “therapeutic,” or “therapy” do not necessarily mean total cure or abolition of the disease or condition. Any alleviation of any undesired signs or symptoms of a disease or condition, to any extent can be considered treatment and/or therapy.

Treatment may include administration of a wound care composition alone or a wound dressing material that has a wound care composition incorporated therein. When used alone, the wound care composition may be administered topically, orally, subcutaneously, or in other means in order to properly treat the wound. When the wound care composition is incorporated into a wound dressing material, the wound dressing material is applied to the wound to treat the wound.

As used herein, a “subject” refers to an animal that is the object of treatment, observation or experiment. “Animal” includes cold- and warm-blooded vertebrates and invertebrates such as fish, shellfish, reptiles and, in particular, mammals. “Mammal” includes, without limitation, mice, rats, rabbits, guinea pigs, dogs, cats, sheep, goats, cows, horses, primates, such as monkeys, chimpanzees, and apes, and, in particular, humans. A subject in need includes a subject that is suffering from a wound, including a burn (including a severe, moderate, or minor burn), trauma, surgical wound, a laceration, a lesion, an ulcer, or a sore. In some embodiments, the subject suffers from a diabetic foot ulcer.

As used herein, the term “prevention” refers to any activity that reduces the burden of the individual later expressing wound symptoms. This can take place at primary, secondary, and/or tertiary prevention levels, wherein: a) primary prevention avoids the development of symptoms/condition; b) secondary prevention activities are aimed at early stages of the condition/symptom treatment, thereby increasing opportunities for interventions to prevent progression of the condition/symptom and emergence of symptoms; and c) tertiary prevention reduces the negative impact of an already established condition/symptom by, for example, restoring function and/or reducing any condition/symptom or related complications.

The articles “a” and “an” are used herein to refer to one or to more than one (to at least one) of the grammatical object of the article. By way of example, “an element” means one element or more than one element.

By “about” is meant a quantity, level, value, number, frequency, percentage, dimension, size, amount, weight or length that varies by as much as 30, 25, 20, 15, 10, 9, 8, 7, 6, 5, 4, 3, 2 or 1% to a reference quantity, level, value, number, frequency, percentage, dimension, size, amount, weight or length.

Throughout this specification, unless the context requires otherwise, the words “comprise,” “comprises,” and “comprising” will be understood to imply the inclusion of a stated step or element or group of steps or elements but not the exclusion of any other step or element or group of steps or elements.

By “consisting of” is meant including, and limited to, whatever follows the phrase “consisting of.” Thus, the phrase “consisting of” indicates that the listed elements are required or mandatory, and that no other elements may be present. By “consisting essentially of” is meant including any elements listed after the phrase and limited to other elements that do not interfere with or contribute to the activity or action specified in the disclosure for the listed elements. Thus, the phrase “consisting essentially of” indicates that the listed elements are required or mandatory, but that other elements are optional and may or may not be present depending upon whether or not they materially affect the activity or action of the listed elements.

In certain embodiments, the “purity” of any given agent in a composition may be specifically defined. For instance, certain compositions may include, for example, an agent that is at least 80, 85, 90, 91, 92, 93, 94, 95, 96, 97, 98, 99, or 100% pure, including all decimals in between, as measured, for example and by no means limiting, by high pressure liquid chromatography (HPLC), a well-known form of column chromatography used frequently in biochemistry and analytical chemistry to separate, identify, and quantify compounds.

EXAMPLES

Some aspects of the embodiments discussed above are disclosed in further detail in the following examples, which are not in any way intended to limit the scope of the present disclosure. Those in the art will appreciate that many other embodiments also fall within the scope of the disclosure, as it is described herein above and in the claims.

Example 1: Choline Geranate Synthesis and Preparation

The following example demonstrates one embodiment of a method of synthesizing CAGE for use in an IL-incorporated wound dressing.

CAGE was synthesized from commercially available reagents using equipment standard to the organic chemistry laboratory. Geranic acid typically requires purification via recrystallization from acetone. The product was characterized with standard methods (including, for example, NMR, UV, or IR) to verify purity. CAGE was synthesized through salt metathesis of 1:2 molar ratio choline bicarbonate and geranic acid, and the final product possessed both fluidity and transparency at room temperature. Two equivalents of neat geranic acid (50.0 g, 0.297 moles, Sigma-Aldrich, St. Louis, Mo.), were recrystallized five times at −70° C. in acetone, in a 500-mL round bottom flask and added to one equivalent of choline bicarbonate (80 wt % solution, 30.7 g, 0.149 moles, Sigma-Aldrich, St. Louis, Mo.). The mixture was stirred at room temperature until CO₂ evolution ceased. Residual H₂O was removed by rotary evaporation at 60° C. for 2 h and drying in a vacuum oven for 24 h at 60° C.

Physical characterization at 25° C. was in good agreement with published values and was as follows: density, 0.989±0.001 g mL⁻¹; and conductivity, 0.0427±0.0005 mS cm⁻¹.

Physicochemical properties were identical to those previously published confirming purity (Zakrewsky et al., PNAS, 2014, 111, 13313; incorporated by reference herein in its entirety, and for the disclosure referenced herein). CAGE has unique properties based upon the 1:1:1 ratio of cation:anion:protonated acid. This is important since it gives rise to the low conductivity determined for CAGE (0.043 mS cm⁻¹) and is a potential indicator of anti-biofilm efficacy but, also provides insight to minimized skin irritation potential.

Composition was confirmed with nuclear magnetic resonance spectroscopy (NMR). NMR assignments were also in good agreement with published assignments and were as follows: ¹H NMR (DMSO-d₆), δ 5.57 (s, 2H), 5.07 (t, J=6.1, 2H), 3.85 (t, J=6.6, 2H), 3.42 (t, J=6.6, 2H), 3.17 (s, 9H), 2.60 (m, 4H), 2.00 (m, 4H), 1.93 (s, 6H), 1.70 (s, 2H), 1.64 (s, 6H), and 1.57 (s, 6H); ¹³C NMR (DMSO-d₆), δ 170.3, 150.4, 131.5, 124.0, 121.7, 67.6, 55.6, 53.5, 40.4, 32.8, 25.8, and 17.8.

CAGE may be incorporated into a wound care composition, such as a dressing or bandage. For example, CAGE may be deposited onto the surface of medical-grade gauze using standard dip-coating protocols. Application of the IL at various concentrations (μmol per cm²) is established by dissolving the IL into an appropriate solvent (e.g. acetone) at various concentrations after which the dressings are coated and allowed to dry. Exemplary IL concentrations include 0.005, 0.006, 0.007, 0.008, 0.009, 0.01, 0.02, 0.03, 0.04, 0.05, 0.06, 0.07, 0.08, 0.09, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, or 2% volume of wound care composition/weight wound dressing material (vol/w %), or greater, such as 3, 4, 5, 6, 7, 8, 9, 10, 15, 20, 30, 40, or 50% vol/w, or an amount within a range defined by any two of the aforementioned values. In some embodiments, the wound care composition is present in an amount of about 0.625% vol/w %. In some embodiments, the amount of IL incorporated into an electrospun scaffold can be 0.01% w/w to about 99% w/w, such as 0.01, 0.05, 0.1, 0.5, 1.0, 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70, 75, 80, 85, or 90, 95, or 99% w/w or greater, or a value within a range defined by any two of the aforementioned values. In some embodiments, the IL is present in an amount of about 40% w/v.

Extraction of a defined weight of the gauze, followed by gravimetric and/or HPLC analysis (with a geranic acid standard) may be used to verify deposition of the appropriate amounts of IL within this procedure. CAGE is unreactive toward the cotton fibers in gauze, but effects (if any) of the deposition on various material may be determined by analysis of treated and un-treated samples with SEM.

Example 2: Electrospinning of IL-Incorporated Wound Dressings

The following example demonstrates one embodiment of a method for electrospinning IL-incorporated wound dressings.

Ionic liquids are incorporated into a protein solution and electrospun onto targets to create novel wound dressings that include CAGE, thereby forming IL wound dressings. The resulting scaffolds are evaluated using SEM for porosity and fiber diameter and compared to known control scaffolds to understand how the inclusion of CAGE affects the architecture of the scaffold. Additionally, mechanical strength testing and characterization are also performed on the IL wound dressing. Last, using HPLC techniques, the inclusion of IL into the wound dressing is confirmed.

Electrospinning was performed under various conditions, as set forth in Table 1. All samples were performed at 26° C., 18% humidity, and at a flow rate of 1 mL/hr. The distance refers to the distance from the electrospinning needle to the target. The % IL refers to the final percentage in the product.

TABLE 1 Electrospinning Conditions % Ionic Liquid % Gelatin Voltage Distance (w/w) (w/v) (V) (cm) 1 0 10 30 12 2 0.2 10 25 9 3 0.7 10 25 9 4 1.0 10 25 9

FIGS. 6A-6B show the product that result from each of the conditions shown in Table 1.

The purpose of this experiment was to manipulate the concentration of IL, CAGE, within a 5 mL, 10% gelatin in hexafluoro-2-propanol (HFIP) solution to effectively incorporate the IL into a final electrospun gelatin scaffold, in the effort of providing the scaffold with an antimicrobial aspect. HFIP is toxic and corrosive.

The method of electrospinning was carried out with a 0.02% w/w concentration of IL in liquid mixture (0.2% w/w concentration of IL in product). 0.5001 g of solid gelatin was weighed out and placed into a glass bottle along with a magnetic stir bar. Next, 5 mL of HFIP was added to the bottle with the gelatin. The bottle was then covered completely with aluminum foil to inhibit the IL from reacting with the light upon being added to the solution. One μL of IL was then added to the bottle using a 1 μL-10 μL pipette; the tip was removed after the IL was dispensed, and a 5 mL syringe was used to push air through the tip in an effort to release any liquid IL remaining in the tip. The bottle was capped and placed in a water bath on top of a stir/heat plate. The temperature of the bath was monitored to ensure it did not exceed 40° C. (human body temperature). The solution was stirred for approximately 30 minutes, where the heat was set to “low” while the stir speed was set to about four. The entire bath was covered with foil and the laboratory lights were shut off during this period (to avoid light exposure of the IL). Once the solution was mixed, until it was a homogeneous mixture, it was placed in the fridge overnight. The gelatin solution was stirred again for about twenty minutes prior to electrospinning.

The solution containing 0.02% w/w IL (liquid form) was electrospun following the general protocol for electrospinning, while the parameters were as follows: temperature, 26° C.; humidity, 19%; distance from needle to target, 9 cm; voltage, 25V; flow rate, 1 mL/hr.

Once the process commenced, the aluminum target was not immediately covered with visible white solid product (FIG. 6B) in comparison to a control gelatin solution without the incorporated IL (FIG. 6A). However, once the scaffold's texture appeared to be uneven with drops, concentrated product spread throughout the scaffold. Because ILs are extremely conductive, the “crackling” sound of the electricity throughout the system was increased, in comparison to electrospinning a control.

Once an hour had passed while electrospinning, the gelatin scaffold with 0.2% IL was placed in a desiccator for twenty-four hours to ensure that the scaffold completely dried.

Data/Calculations (0.2% Ionic Liquid in Final Product)

Mass of gelatin: 0.5001 g

Volume of HFIP: 5 mL

Volume of ionic liquid: 1 μL (0.2% in product)

Percent weight/volume (for mass of gelatin and volume of HFIP)

10%=10 g/100 mL

0.5 g gelatin/5 mL HFIP

For volume/concentration of ionic liquid: 5 mL (total volume)×0.2% (desired concentration of ionic liquid in product)=1.0 μL ionic liquid.

FIG. 6B shows the 0.2% ionic liquid-concentrated gelatin scaffold being electrospun.

The same procedure used for the 10% gelatin scaffold in 5 mL HFIP with 0.2% incorporated IL may be used to create additional mixtures with IL, for example, with concentrations of 0.7% and 1.0% IL in the final gelatin scaffolds. The parameters for electrospinning were kept the same for these additional mixtures. A control scaffold was also spun, with the same amount of gelatin in HFIP. The distance from the needle to the target was returned to 12 cm for the control.

Data/Calculations (0.7% Ionic Liquid in Final Product)

Mass of gelatin: 0.5006 g

Volume of HFIP: 5 mL

Volume of ionic liquid: 3.5 μL

Percent weight/volume

10%=10 g/100 mL

0.5 g gelatin/5 mL HFIP

For volume/concentration of ionic liquid: 5 mL (total volume)×0.7% (desired concentration of ionic liquid in product)=3.5 μL ionic liquid.

Similar to the first IL-concentrated solution that was spun, the aluminum target turned white after a longer period than normal. The sound of the electricity again was more prominent than with a control, but not much different from the first IL-spun scaffold. The texture of the final product was not as smooth as a control scaffold, with more droplet-structures upon the surface, as shown in FIG. 6C.

Data/Calculations (1.0% Ionic Liquid in Final Product)

Mass of gelatin: 0.5001 g

Volume of HFIP: 5 mL

Volume of ionic liquid: 5.0 μL

Percent weight/volume

10%=10 g/100 mL

0.5 g gelatin/5 mL HFIP

For volume/concentration of ionic liquid: 5 mL (total volume)×1.0% (desired concentration of IL in product)=5.0 μL ionic liquid.

The observation of the loud sound of electricity noted from the two previous scaffolds was again present. However, the target began to turn white quicker, and again, the texture of the final product consisted of droplets instead of being smooth, as shown in FIG. 6D.

Upon removing the scaffolds from the desiccator eight days later, the scaffolds were difficult to remove from the aluminum targets, and therefore came off in broken-up pieces.

NMR Data

FIG. 7 shows the molecular structure of geranate (top left) and choline (top right). The bottom photo is the NMR spectrum showing the presence of the two ions in the gelatin scaffold.

To verify inclusion of CAGE within the IL-incorporated scaffolds, a small portion (˜1 mg) of the dried scaffold material was placed into a test tube along with 0.7 mL of deuterated acetone (acetone-d6, 99.9%, Sigma-Aldrich) and the mixture was incubated overnight at room temperature with periodic mixing. A similar extraction was performed on a control scaffold that was not incorporated with IL. The extracted acetone was removed from the extraction vessel and placed into an NMR tube, and analyzed via ¹H NMR (400 MHz, Bruker). The biological activity of the extracted IL is also assessed using the broth microdilution assay against Staphylococcus aureus and Pseudomonas aeruginosa.

FIG. 8 shows the ¹H NMR spectrum of the extracted scaffold (top) and authentic CAGE (below) in acetone-d6.

As can be seen in FIG. 8, the spectrum for the extracted scaffold shows characteristic resonances associated with the geranate anion/geranic acid (singlets at ˜1.6 and 1.67 ppm, multiplet at 2.0 ppm, singlets at 5.07 and 5.57 ppm) that are similarly observed in the control spectrum. Characteristic resonances of the choline cation are also observed (triplet at 3.85, triplet at 3.42 and singlet at 3.17) in the extracted spectrum, but to a lower molar equivalence than that of the neat CAGE. This is likely due to a relatively inefficient extraction of the choline cation from the scaffold using this particular organic solvent.

Example 3: Efficacy of Ionic Liquid-Incorporated Wound Dressings to Resist Biofouling/Reduce Biofilms

The following example demonstrates the efficacy of the IL-incorporated wound care compositions for the reduction of biofilm formation and the prevention and inhibition of pathogen proliferation and growth in wounds.

The effect of the IL-incorporated dressings either to resist or to treat biofilms was quantified using in vitro assays with pathogens associated with skin wounds (e.g. S. aureus) or diabetic ulcers (e.g. P. aeruginosa). To examine the effect of IL-treatment on the resistance of the dressings to biofouling, small (1 cm² or less) samples of dressings were placed on a solid nutrient medium and inoculated with actively growing bacteria (10⁵ cells). This method parallels a commonly employed assay known as the colony biofilm test (Merritt et al. (2005) Growing and analyzing static biofilms. Current protocols in microbiology Chapter 1:Unit 1B 1; incorporated by reference herein in its entirety). Biofilms were cultured on dressings with various amounts of deposited CAGE and the number of viable cells existing on these surfaces was determined by initial disruption of the biofilm with sonication, followed by dilution and enumeration of the viable bacteria. Biofilm formation was assayed using culture and qPCR of the bacterial populations as a function of IL concentration and time (24 to 72 hrs). Similarly, the ability of the IL-treated dressings to reduce viability in an established biofilm was assessed by overlaying small pieces of dressing upon biofilms that had been previously cultured on a surface of equivalent size; effectiveness was quantified as a function of treated material and length of exposure.

Example 4: CAGE-Incorporated Wound Dressings

The following example demonstrates the efficacy of CAGE-incorporated gauze for the reduction of biofilm formation and the prevention and inhibition of pathogen proliferation and growth.

Gauze was coated with an IL, CAGE, in various concentrations. The CAGE-incorporated gauze was treated with approximately 100 μL of actively growing bacteria, including P. aeruginosa, Enterococcus, K. pneumoniae, or methicillin sensitive S. aureus (MSSA), at 10⁸-10⁹ cells per mL. Each of these bacteria are clinically isolated pathogens commonly associated with wounds and 10⁸-10⁹ cells/mL is a high concentration of live bacteria. In terms of clinical practice, bacterial concentrations in this amount are unlikely to be found, even in cases of septicemia.

As shown in FIGS. 9 through 12, CAGE-incorporated gauze effectively reduced and/or inhibited the growth of bacteria in the gauze. FIGS. 9A and 9B show that the growth of P. aeruginosa was prohibited at both 30 minutes and 2 hours following contact with the gauze when CAGE was present in an amount ranging from 1%-10% (1% is 1.25 μg, 5% is 6.25 μg, and 10% is 12.5 μg CAGE). In contrast, control gauze with no IL incorporation showed elevated bacteria amounts. In addition, the percentage of surviving colonies after contact with CAGE-incorporated gauze was reduced to values of less than about 20% in all treatment groups, as compared to percentage of surviving colonies that were untreated.

Similar results are achieved when the gauze is exposed to Enterococcus (FIGS. 10A and 10B), K. pneumoniae (FIGS. 11A and 11B), and MSSA (FIGS. 12A and 12B).

Example 5: CAGE-Incorporated Scaffolds

The following example demonstrates the efficacy of CAGE-incorporated scaffolds for the reduction of biofilm formation and the prevention and inhibition of pathogen proliferation and growth.

Scaffolds were prepared as described in Example 2, wherein protein was mixed with CAGE to generate a CAGE-incorporated scaffold. The CAGE scaffolds included various concentrations of CAGE from 1% to 10% during the production process (1% is 1.25 μg, 5% is 6.25 μg, and 10% is 12.5 μg CAGE). The CAGE scaffolds were prepared by electrospinning. As shown in FIGS. 13 through 14, CAGE incorporated into protein scaffolds reduced bacteria growth. Specifically, FIGS. 13A and 13B show reduced colony forming units (CFU) of P. aeruginosa in CAGE-incorporated scaffolds (at 10% and 5%) compared to control scaffold with no IL incorporation at both 30 minutes and 2 hours after exposure to the bacteria.

Similarly, FIGS. 14A and 14B show reduced CFU of Enterococcus in CAGE-incorporated scaffolds (at 10% and 5%) compared to control scaffold with no IL incorporation at both 30 minutes and 2 hours after exposure to the bacteria.

FIGS. 15A and 15B show the ability of human dermal neonatal fibroblasts to attach and proliferate in general growth medium to both the surface of control scaffolds (FIG. 15A) and CAGE-incorporated scaffolds (40%) (FIG. 15B). Human dermal neonatal fibroblasts (P9) were added to a well plate containing control scaffolds or scaffolds containing 40% (v/w) CAGE. The control scaffold was UV sterilized prior to seeding cells. These images show that bacteria may be killed without harming or otherwise preventing human cells from proliferating on the surface.

Example 6: Additional IL-Incorporated Scaffolds and IL-Incorporated Wound Dressings

The following provide additional examples of IL compositions for incorporation into scaffolds and wound dressing as described herein.

According to one embodiment, the IL composition comprises choline geranate and a neutral species, such as farnesol, linalool, carvacrol, geranic acid, eugenol, citronellic acid, or cinnamaldehyde. In another embodiment, the IL comprises choline citronellate and a neutral species, such as farnesol, linalool, carvacrol, geranic acid, eugenol, citronellic acid, or cinnamaldehyde.

In another embodiment, an IL-scaffold or IL-wound dressing comprises an analgesic for pain and/or inflammation relief. In a specific embodiment, the scaffold or dressing comprises a cannabinoid compound as described previously. In some embodiments, the compositions further include an antibiotic, a steroid, an analgesic, a cannabinoid compound, and/or a growth factor.

All headings are for the convenience of the reader and should not be used to limit the meaning of the text that follows the heading, unless so specified.

All patents and publications mentioned in the specification are indicative of the levels of those skilled in the art to which the invention pertains. All patents and publications are herein incorporated by reference to the same extent as if each individual publication was specifically and individually indicated to be incorporated by reference, and for any disclosure specifically referenced herein.

While various aspects and embodiments have been disclosed herein, other aspects and embodiments will be apparent to those skilled in the art. The various aspects and embodiments disclosed herein are for purposes of illustration and are not intended to be limiting, with the true scope and spirit being indicated by the claims. 

What is claimed is:
 1. A wound care composition, comprising: an ionic liquid (IL) and a neutral species, wherein the ionic liquid is present in an amount of about 0.01% w/w to about 99% w/w; and a protein scaffold comprising a protein solution.
 2. The wound care composition of claim 1, wherein the IL is choline geranate (CAGE) or choline citronellate.
 3. The wound care composition of claim 1, wherein the wound care composition is incorporated with or impregnated into or coated onto a wound dressing, a bandage, a gauze, a patch, a pad, tape, or a wrap.
 4. The wound care composition of claim 1, wherein the ionic liquid is present in an amount of about 40% w/w.
 5. The wound care composition of claim 1, wherein the protein solution comprises collagen, albumin, casein, fibrin, fibroin, gelatin, keratin, elastin, tropoelastin, or combinations thereof.
 6. The wound care composition of claim 1, wherein the protein scaffold is electrospun.
 7. The wound care composition of claim 1, wherein the protein solution is present in an amount of about 1% w/v to about 20% w/v.
 8. The wound care composition of claim 1, wherein the protein scaffold is present in an amount of about 10% w/v.
 9. The wound care composition of claim 1, comprising IL in an amount of about 0.2% w/w and gelatin in an amount of about 10% w/v gelatin.
 10. The wound care composition of claim 1, wherein the neutral species comprises farnesol, linalool, carvacrol, geranic acid, citronellic acid, cinnamaldehyde, eugenol, or combinations thereof.
 11. The wound care composition of claim 1, further comprising an antibiotic, a steroid, an analgesic, a cannabinoid, a growth factor, or a combination thereof.
 12. A wound dressing comprising: a wound care composition of claim 1; and a wound dressing material.
 13. The wound dressing of claim 12, wherein the wound dressing material is a bandage, a wipe, a sponge, a mesh, a dressing, a gauze, a patch, a pad, tape, or a wrap.
 14. The wound dressing of claim 12, wherein the wound care composition is present in an amount of about 0.005% v/w to about 2% v/w.
 15. The wound dressing of claim 12, wherein the wound care composition is present in an amount of about 0.625% v/w.
 16. The wound dressing of claim 12, wherein the wound care composition is incorporated into or coated onto or impregnated with the wound dressing material. 